PRIME TPO E-2900H
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | PRIME TPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WdI4BA_PRIME-TPO-E-2900H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRIME TPO E-2900H is a Polypropylene Homopolymer (PP Homopolymer) product. It is available in Asia Pacific, Europe, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 19.5 | MPa | |
| Break | 24.0 | MPa | |
| Tensile Strain (Break) | < 500 | % | ISO 527-2 |
| Flexural Modulus | 590 | MPa | ISO 178 |
| Flexural Stress | 21.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 80 | µm | |
| Tensile Modulus | JIS Z1702 | ||
| MD : 80 µm | 550 | MPa | |
| TD : 80 µm | 550 | MPa | |
| Tensile Stress | JIS Z1702 | ||
| MD : Break, 80 µm | 43.0 | MPa | |
| TD : Break, 80 µm | 43.0 | MPa | |
| Tensile Elongation | JIS Z1702 | ||
| MD : Break, 80 µm | < 500 | % | |
| TD : Break, 80 µm | < 500 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 10 | kJ/m² | ISO 180 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | JIS K7105 | ||
| 80.0 µm 1 | 0.70 | % | |
| 80.0 µm 2 | 9.0 | % |
| Note Message | |
|---|---|
| 1 . | Internal |
| 2 . | All |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hostaform® C 9021 K | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Kuraray Poval® LM-10HD | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| INNOPOL® PP CS 2-9523 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |
| Lupolen 2420 H | LyondellBasell Industries | LDPE | Lupolen |
| Akulon® FC-X9201 | DSM Engineering Plastics | Nylon 6 | Akulon® |