| PC/ABS alloy, talc filled grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Ash Content | 20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4100 | MPa | ASTM D638 |
| Tensile Strength (Break) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 115 | °C | ASTM D648 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 250 | °C | |
| Front Temperature | 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sympoxy™ 1230/284 | Hapco Inc. | Epoxy | Sympoxy™ |
| Celstran® PP-GF30-0553 Black | Celanese Corporation | PP Copolymer | Celstran® |
| Fainplast PVC GS 87/BT | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Karina LILAC PVC COMP -E KAPU 6534/190-NT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Softell TKG 300N C12453 | LyondellBasell Industries | PP Copolymer | Softell |