HiFill® PA6 CF20 RM BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WcrKn8_HiFill-PA6-CF20-RM-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PA6 CF20 RM BK is a Polyamide 6 (Nylon 6) product filled with 20% carbon fiber. It can be processed by injection molding and is available in North America. Primary characteristic: low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 138 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| TPCI # | 9720102 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 260 to 304 | °C | |
| Processing (Melt) Temp | 243 to 271 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3483-3 | RTP Company | LCP | RTP |
| VINIKA® D3058 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| 4TECH® 9A22730 H | 4Plas | Nylon 66 | 4TECH® |
| Ebalta GH 767 / GL | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Karina CLEAR PVC COMP. -E 87/206-D-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |