Infino TK-2050H
| Category: | PCT , Polycyclohexylenedimethylene Terephthalate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WclGlU_InfinoTK2050H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino TK-2050H is a polycyclohexyldimethyl terephthalate (PCT) product, which contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: mirrors. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.79 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 35 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.49 - 0.59 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.50 - 0.62 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.50 - 0.62 | % | ISO 2577 |
| Traffic : 3.20mm | 0.49 - 0.59 | % | ISO 2577 |
| Ash Content | |||
| -- | 51 | % | ASTM D5630 |
| -- | 51 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 119 | ASTM D785 | |
| R scale | 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4780 | MPa | ASTM D638 |
| -- | 6050 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 58.8 | MPa | ASTM D638 |
| Yield | 57.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 58.8 | MPa | ASTM D638 |
| Fracture | 57.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 2.1 | % | ASTM D638 |
| Fracture | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus 5 | |||
| -- | 6370 | MPa | ASTM D790 |
| -- | 6960 | MPa | ISO 178 |
| Flexural Strength 6 | |||
| -- | 71.6 | MPa | ASTM D790 |
| -- | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 2.7 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 8(23°C) | 12 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 23 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 22 | J/m | ASTM D256 |
| 23°C 9 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C, 3.18 mm | 170 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 170 | J/m | ASTM D256 |
| -5°C 10 | 11 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 240 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 240 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 203 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Thickness: 4mm |
| 8 . | Thickness: 4mm |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUNFROST® KD90EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| Monprene® CE-922968 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Sylvin 4200-88 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SABIC® BR 4010 | Saudi Basic Industries Corporation (SABIC) | PBR, High Cis | SABIC® BR |
| CERTENE™ PHF-4 | Muehlstein | PP, HMS | CERTENE™ |