Prime Polypro™ J-700GP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | Prime Polypro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Wc7XZv_Prime-Polypro-J-700GP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Prime Polypro™ J-700GP is a Polypropylene Homopolymer (PP Homopolymer) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Primary characteristic: homopolymer. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.4 to 1.8 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 96 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1350 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 200 | % | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Flexural Stress | 41.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 4.2 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 93.0 | °C | ISO 75-2/B |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss | 80 | ASTM D2457 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 802 TFE 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| T-Blend® 7500N-FM | TSRC Corporation | SEBS | T-Blend® |
| Bio-Flex® F 1137 | FKuR Kunststoff GmbH | PLA | Bio-Flex® |
| PAXOTHENE® NA208 | USI Corporation | LDPE | PAXOTHENE® |
| Dutral® OCP 2550 | Versalis S.p.A. | EPDM | Dutral® |