Wellamid® FRGF25-66-N is a Polyamide 66 (Nylon 66) material filled with 25% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Wellamid® FRGF25-66-N are:
Typical application of Wellamid® FRGF25-66-N: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.0 to 1.4 | % | |
| Flow : 23°C | 0.30 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 110 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 6900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 160 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 3.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 271 to 282 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Nozzle Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 6088 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Fainplast PVC GK 77/R1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Huafon JF-A-5030 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| MAJORIS BE084 | AD majoris | PP, Unspecified | MAJORIS |
| OxyVinyls® 500F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |