ISPLEN® PM 274 AT
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WXasdY_ISPLEN-PM-274-AT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer, 20% mineral fillers reinforced and high melt flow rate. ISPLEN® PM274 AT shows a good compromise between impact strength and stiffness, keeping a low warpage and shrinkage behaviour. The product is high heat stabilised. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.87 to 0.88 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1850 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 25.0 | MPa | |
| Break | 19.5 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.5 | % | |
| Break | 22 | % | |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 2.0 | kJ/m² | |
| -20°C | 2.0 | kJ/m² | |
| 0°C | 3.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 21 | kJ/m² | |
| -20°C | 25 | kJ/m² | |
| 0°C | 35 | kJ/m² | |
| 23°C | 57 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 74.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 147 | °C | ISO 306/A120 |
| -- | 75.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 681 | RTP Company | ABS | RTP |
| RheTech Polypropylene HP525-283UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sylvin 8658-70 Grey 9510 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Badamid® A70 TM-Z1 | Bada AG | Nylon 66 | Badamid® |
| EMOPLEN® A 1503 T4 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |