Hostaform® UV90Z XAP2 ™
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WWLwUf_HostaformUV90ZXAP2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Preliminary Data Sheet Hostaform® acetal copolymer grade UV90Z XAP2 ™ is a UV stabilized material available in a range of colors generally for automotive interior applications. In addition, Hostaform® UV90Z XAP2 ™ has lower emissions as required for some automotive interiors. Low Emission Performance [VDA-275] <5 PPM |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.7 | % | ISO 294-4 |
| Flow | 2.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2650 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 64.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 167 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 165 - 175 | °C | |
| Middle Temperature | 170 - 180 | °C | |
| Front Temperature | 170 - 180 | °C | |
| Nozzle Temperature | 180 - 190 | °C | |
| Processing (Melt) Temp | 180 - 190 | °C | |
| Mold Temperature | 80 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 4.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 180 to 200°CZone 4 Temperature: 175 to 185°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SEV-3900M80 | SHIN-A T&C | Epoxy | SHIN-A |
| Andur M-11 (97% HQEE/ 3% TMP) | Anderson Development Company | PUR-Ester/MDI | Andur |
| Grupo IDESA HIPS HI-730-S-02 | Grupo IDESA, S.A. de C.V. | SBC | Grupo IDESA HIPS |
| KOCETAL® WR301LOGR | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Parylene HT® | Specialty Coating Systems (SCS) | PPX | Parylene |