Propafilm™ RC240
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WW6sba_Propafilm-RC240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Acrylic Coated Film Biaxially oriented polypropylene (BOPP) film coated on both sides with an aqueous acrylic (chlorine free) dispersion. RC200/240 are suitable for heavy duty applications where the films' excellent hot-tack and seal threshold can give superior machine performance over alternative structures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 121°C, 1 min | 2.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 6100 | µm | |
| Seal Strength 1 | 0.15 | N/mm | Internal Method |
| Seal Initiation Temperature 2 | 85.0 to 146 | °C | Internal Method |
| Oxygen Permeability (25°C, 0% RH) | 14 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 2.9 | g/m²/24 hr | ASTM F1770 |
| Yield | 18.3 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 95 | ASTM D2457 | |
| Haze 3 | 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 265°F; 2secs; 15psi |
| 2 . | 2secs; 15psi |
| 3 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Talcoprene® 1540TLT NERO | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| U-polymer U-8000 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| Capilene® QE 73 B | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |
| ELASTOSIL® RT K | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Sylvin 8707-84 Blue 8491 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |