PTS PCA-2201NH
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | PTS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WVw0M7_PTS-PCA-2201NH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PTS PCA-2201NH is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/3.8 kg | 12 | g/10 min | |
| 260°C/2.16 kg | 16 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 3.17 mm) | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.18 mm) | 65 | % | ASTM D638 |
| Flexural Modulus (3.17 mm) | 2690 | MPa | ASTM D790 |
| Flexural Strength (3.17 mm) | 88.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.17 mm) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | > 600 | V | UL 746 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | 60.0 to 120 | ||
| 2.50 mm | 60.0 to 120 | ||
| 3.00 mm | 60.0 to 120 | ||
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 1 | ||
| 2.50 mm | PLC 1 | ||
| 3.00 mm | PLC 1 | ||
| High Voltage Arc Tracking Rate (HVTR) | 80.0 to 150 | mm/min | UL 746 |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | 15 to 30 | sec | |
| 2.50 mm | 15 to 30 | sec | |
| 3.00 mm | 30 to 60 | sec | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | ||
| 2.50 mm | PLC 3 | ||
| 3.00 mm | PLC 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 925 | °C | |
| 2.00 mm | 925 | °C | |
| 3.00 mm | 950 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 700 | °C | |
| 2.00 mm | 700 | °C | |
| 3.00 mm | 700 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209A Z | RTP Company | Nylon 6 | RTP |
| Gallonprene® GP550-7004 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Plexiglas® V825 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Polifil® Nylon 625L | The Plastics Group | Nylon 66 | Polifil® Nylon |
| Sylvin 6232-78 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |