Panlite® B-8130R
| Category: | PC , Polycarbonate |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WV4LXb_Panlite-B-8130R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon fiber reinforced grades-30% Carbon fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.30 to 0.50 | % | |
| Flow : 4.00 mm | 0.010 to 0.15 | % | |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 16000 | MPa | ISO 178 |
| Flexural Stress 2 | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 20 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 149 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 147 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 153 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.0E-5 | cm/cm/°C | |
| Transverse | 5.0E-5 | cm/cm/°C | |
| RTI Elec (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 to 10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0 to 1.0E+2 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 3.00 mm | V-1 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LAF423C | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Thermylene® P-30TC-1156 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Gravi-Tech™ GT6200-5002 X4 Black | PolyOne Corporation | Nylon 12 | Gravi-Tech™ |
| TECHNYL® B 738 MX15 GREY 3279 | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® |
| Osterlene® PPH18F | Osterman & Company | PP Homopolymer | Osterlene® |