Vyncolit® 3640CG
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WTMgG0_Vyncolit-3640CG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® 3640CG is a graphite filled phenolic molding compound with excellent dimensional stability and special tribological properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| Apparent Density | 0.92 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.49 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Post Shrinkage | 0.060 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.56 | % | ISO 178 |
| Tensile Modulus (Injection Molded) | 18000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 47.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 0.29 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 16000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 79.0 | MPa | ISO 178 |
| Compressive Stress | 99.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 1.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Injection Molded) | 2.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 146 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.5E-5 | cm/cm/°C | TMA |
| Lateral | 3.5E-5 | cm/cm/°C | TMA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa |
| Injection instructions |
|---|
| Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 8020/60 | Wacker Chemie AG | Silicone | SILPURAN® |
| NEFTEKHIM PP 5210M (RCXP721) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| IROGRAN® A 60 E 4902 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| POLYFLAM® RPP 4220 CS1 | A. Schulman Europe | PP Homopolymer | POLYFLAM® |
| LEXAN™ LUX9132C resin | SABIC Innovative Plastics | PC | LEXAN™ |