Delrin® 100PE NC010
| Category: | Acetal (POM) Homopolymer , ACETAL RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Delrin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WRfF6Z_Delrin-100PE-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Viscosity Acetal Homopolymer with Very Low Emissions |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 2.10 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.8 | % | |
| Flow | 2.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M-Scale | 91 | ||
| R-Scale | 121 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 72.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 26 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 45 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 400 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 157 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 99.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Flow : -40 to 23°C | 1.0E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 23°C | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 44 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.00 | ||
| 1 MHz | 3.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 5.0E-4 | ||
| 1 MHz | 5.0E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.19 | g/cm³ |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | < 2.00 | mg/kg | VDA 275 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN M7392(U) | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Bapolan® PS6460 | Bamberger Polymers, Inc. | PS (HIPS) | Bapolan® |
| Braskem PP C715-12NHP | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| Clariant Nylon 6/6 6608M33-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| MAXATEL® AH100T-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |