AGILITY™ 1021 Performance LDPE is a high pressure LDPE resin designed to run at faster output rates on blown film lines in LLDPE rich blends while maintaining optics. Main Characteristics: Faster processing LDPE resin Designed for higher output rates in blends with LLDPE resins at 20-30% loading - Optimized molecular structure gives improved optics in blends with LLDPE resins Complies with: EU No 10/2011 U.S.FDA 21 CFR 177.1520 (c) 2.2 Canadian HPFB No Objection Consult the regulations for complete details

General Information
Agency Ratings	FDA 21 CFR 177.1520(c) 2.2 HPFB (Canada) No Objection Europe No 10/2011
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.919	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.9	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	51	µm
Film Puncture Resistance (51 µm)	4.87	J/cm³	Internal method
Film strength			ASTM D882
MD : 51 µm	45.8	J/cm³	ASTM D882
TD : 51 µm	60.1	J/cm³	ASTM D882
secant modulus			ASTM D882
2% secant, MD : 51 µm	168	MPa	ASTM D882
2% secant, TD : 51 µm	185	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield, 51 µm	10.9	MPa	ASTM D882
TD : Yield, 51 µm	10.8	MPa	ASTM D882
MD : Fracture, 51 µm	21.6	MPa	ASTM D882
TD : Fracture, 51 µm	16.4	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture, 51 µm	260	%	ASTM D882
TD : Fracture, 51 µm	540	%	ASTM D882
Dart Drop Impact (51 µm)	100	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 51 µm	460	g	ASTM D1922
TD : 51 µm	250	g	ASTM D1922

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	108	°C	Internal method

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 50.8 µm)	60		ASTM D2457
Haze (50.8 µm)	9.0	%	ASTM D1003

Extrusion instructions
Fabrication Conditions For Blown Film: Screw Size: 3.5 in.; 30:1 ratio L/D Screw Type: DSB II Die Gap: 70 mil (1.78 mm) Melt Temperature: 404°F (206°C) Output: 16 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 50 rpm Frost Line Height: 42 in. (1067 mm) IBC

Resin Grade	Manufacturer	Category	Trademark
Prime ABS Weather-X 200	Primex Plastics Corporation	ABS+Acrylic	Prime ABS Weather-X
Veroplas SKG20	PlastxWorld Inc.	ABS	Veroplas
APEX® 77-W002-F	Teknor Apex Company	PVC, Flexible	APEX®
POLYCOMPO PP F102W	POLYCOMPO Co.,Ltd.	PP, Unspecified	POLYCOMPO PP
ALTECH® PA6 ECO 2035/507 GF35	ALBIS PLASTIC GmbH	Nylon 6	ALTECH® PA6