Styrolux® 693D
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolux® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WQP6Hm_Styrolux-693D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Styrolux® 693D is a clear styrene-butadiene copolymer (SBC) with a well balanced combination of toughness and clarity. Styrolux 693D is mainly used for thermoformed articles, especially in blends with general-purpose polystyrene. Styrolux 693D contains a microcrystalline wax which acts as an antiblock providing processing benefits but decreases the printability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 12.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.30 to 1.0 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.2 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 260 | % | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Flexural Stress | |||
| 5.0% Strain | 32.0 | MPa | |
| -- | 32.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation - MD (Break) | 260 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 2.5 | kJ/m² | |
| 23°C | 3.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 72.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 59.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 76.0 | °C | ISO 306/A50 |
| -- | 48.0 | °C | ISO 306/B50 |
| CLTE - Flow | 6.0E-5 to 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant (100 Hz) | 2.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.0E-4 | ||
| 1 MHz | 8.0E-4 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.570 | ISO 489 | |
| Transmittance (550 nm) | 89.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 to 250 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2283 | RTP Company | PEEK | RTP |
| S&E Automotive XP11-289A15 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Trexprene® A88BW-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| LNP™ COLORCOMP™ G1000 compound | SABIC Innovative Plastics | PSU | LNP™ COLORCOMP™ |
| LTP ZC-1600B | Chengdu Letian Plastics Co., Ltd | PPS | LTP |