TOTAL Polyethylene L 425
| Category: | mPE , Metallocene Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WPkXua_TOTALPolyethyleneL425.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
L425: Blown film polyethylene grade. Provides excellent bubble stability, exceptional tear strength, high impact and puncture resistance, outstanding clarity and gloss, good stiffness, excellent compatibility with LDPE and LLDPE. Applications: L425 is recommended for shrink films, heavy duty sacks, food packaging, laminations and multilayer packaging film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.925 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.40 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 12 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882A | ||
| 1% secant, MD : 25 µm, blown film | 228 | MPa | ASTM D882A |
| 1% secant, TD : 25 µm, blown film | 234 | MPa | ASTM D882A |
| Tensile Strength | ASTM D882A | ||
| MD : Broken, 25 µm, blown film | 44.8 | MPa | ASTM D882A |
| TD : Broken, 25 µm, blown film | 41.4 | MPa | ASTM D882A |
| Tensile Elongation | ASTM D882A | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882A |
| TD : Broken, 25 µm, blown film | 800 | % | ASTM D882A |
| Dart Drop Impact (25 µm, Blown Film) | 300 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 350 | g | ASTM D1922 |
| TD : 25 µm, blown film | 800 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 120 | °C | ASTM D3417 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (45°, 25.4 µm, Blown Film) | 60 | ASTM D523 | |
| Haze (25.4 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 34S5150 | The Matrixx Group, Inc. | PBT | Matrixx |
| Maxelast® P3875H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sylvin 86017-50 Red 6238 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| BJB Polyurethane TC-644 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| PENTAMID B GV30 E H schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |