Grilamid® LCL-3 H anthracite
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WOb1gG_Grilamid-LCL-3-H-anthracite.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilamid® LCL-3 H anthracite is a Polyamide 12 (Nylon 12) material filled with 30% long carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grilamid® LCL-3 H anthracite are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Across Flow | 0.10 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 1.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | -- | 135 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | -- | 19000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | -- | 250 | MPa | ISO 527-2 |
| Tensile Strain (Break) | -- | 1.7 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | -- | 28 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | -- | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 170 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 160 | -- | °C | ISO 75-2/C |
| Melting Temperature 1 | 178 | -- | °C | ISO 11357-3 |
| CLTE - Transverse | 5.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 50 | ohms | IEC 60093 |
| Volume Resistivity | -- | 1.0E+4 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA12, MH, 14-190N, CF30 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ NT-818.G002-8000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Resiten® LFBI | ITEN INDUSTRIES | Phenolic | Resiten® |
| Multi-Flex® TPE A9002 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| EPAMOULD 650D55 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| LNP™ STAT-LOY™ YX02589C compound | SABIC Innovative Plastics | TPEE | LNP™ STAT-LOY™ |