Amilan® CM1011G-15
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WOBzGL_Amilan-CM1011G-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Amilan® CM1011G-15 is a Polyamide 6 (Nylon 6) product filled with 15% glass fiber. It is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 0.70 to 1.1 | -- | % | |
| Flow : 3.00 mm 2 | 0.50 to 0.70 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.3 | -- | % | |
| Saturation, 23°C | 8.3 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C | 90 | -- | ||
| R-Scale, 23°C | 119 | -- | ||
| R-Scale, 80°C | 10 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 150 | 120 | MPa | |
| 23°C | 130 | 65.0 | MPa | |
| 80°C | 55.0 | 30.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 2.0 | 5.0 | % | |
| Break, 23°C | 2.5 | 6.0 | % | |
| Break, 80°C | 6.0 | 7.5 | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 7300 | 5900 | MPa | |
| 23°C | 5800 | 2700 | MPa | |
| 80°C | 2300 | 1700 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 245 | -- | MPa | |
| 23°C | 200 | 100 | MPa | |
| 80°C | 100 | 50.0 | MPa | |
| Compressive Stress | ISO 604 | |||
| -40°C | 220 | 140 | MPa | |
| 23°C | 150 | 75.0 | MPa | |
| 80°C | 85.0 | 45.0 | MPa | |
| Shear Strength (23°C) | 105 | -- | MPa | ASTM D732 |
| Taber Abrasion Resistance (1000 Cycles) | 0.300 | -- | mg | ISO 9352 |
| Coefficient of Friction - vs. Metal 3 | 0.150 | -- | Suzuki Method |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 6.0 | 7.0 | kJ/m² | |
| 23°C | 9.0 | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | 20 | 25 | kJ/m² | |
| 23°C | 50 | 60 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 210 | -- | °C | ISO 75-2/B |
| Melting Temperature | 225 | -- | °C | DSC |
| CLTE - Flow | 4.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1700 | -- | J/kg/°C | |
| Thermal Conductivity | 0.31 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant 4 | IEC 60250 | |||
| 23°C, 50 Hz | 4.50 | -- | ||
| 23°C, 1 kHz | 4.30 | -- | ||
| 23°C, 1 MHz | 3.70 | -- | ||
| Dissipation Factor 5 | IEC 60250 | |||
| 23°C, 50 Hz | 0.050 | -- | ||
| 23°C, 1 kHz | 0.040 | -- | ||
| 23°C, 1 MHz | 0.030 | -- | ||
| Arc Resistance 6 | 120 | -- | sec | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | Without Lubrication |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T40P105-04 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Vipel® F085-CCC-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| AIE PC/ABS A2200FR-3070 | Asia International Enterprise (Hong Kong) Limited | PC+ABS | AIE PC/ABS |
| INEOS PP 100-GD02 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| Polipom 20D | Poliblend S.p.a. | Acetal (POM) Homopolymer | Polipom |