Estane® 58212 TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WL3CG0_Estane-58212-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® 58212 is a 95A Polyether-type thermoplastic polyurethane (TPU) compound. Features: Excellent clarity and UV stable with good melt strength. Pre-drying: 2 hours at 104°C (220°F) in dehumidifying hopper dryer Uses: Extrusion: Cable jacket, hose/tube, profile and film and sheet |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 92 - 98 | ASTM D2240 | |
| Shaw D | 43 - 49 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 51.7 | MPa | ASTM D638 |
| 100% strain | 13.5 | MPa | ASTM D638 |
| 300% strain | 31.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 400 | % | ASTM D638 |
| Flexural Modulus (23°C) | 76.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 5.00 | mg | ASTM D3389 |
| Modulus of Rigidity | ASTM D1053 | ||
| -50°C | 366 | MPa | ASTM D1053 |
| -40°C | 214 | MPa | ASTM D1053 |
| -20°C | 41.3 | MPa | ASTM D1053 |
| 0°C | 13.8 | MPa | ASTM D1053 |
| 23°C | 8.40 | MPa | ASTM D1053 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (200% Strain) | 20 | % | ASTM D412 |
| Tensile Stress | ASTM D412 | ||
| 100% strain | 13.5 | MPa | ASTM D412 |
| 300% strain | 31.6 | MPa | ASTM D412 |
| Tensile Strength (Break) | 51.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 118 | kN/m | ASTM D624 |
| Cracking | 29 | kN/m | ASTM D470 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 36 | % | ASTM D395 |
| 70°C, 22 hr | 61 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -25.0 | °C | DSC |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 182 - 188 | °C | |
| Cylinder Zone 2 Temp. | 188 - 199 | °C | |
| Cylinder Zone 3 Temp. | 193 - 204 | °C | |
| Cylinder Zone 4 Temp. | 199 - 210 | °C | |
| Adapter Temperature | 204 - 216 | °C | |
| Die Temperature | 193 - 210 | °C |
| Extrusion instructions |
|---|
| Screens: 20-40-80-20 meshFeed Throat Cooling: YesScrew Cooling: NoScrew Speed: 15 to 70 rpm |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ AS-XC588 BLU 436C | PolyOne Corporation | ABS | Stat-Tech™ |
| Vi-Chem PVC VNC85-30I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| UBE Nylon 5034 MTX1 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| Nylene® 721 | Custom Resins Group | Nylon 6 | Nylene® |
| Hyundai EP PPF HT980 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |