Polypropylene self-extinguishing compound, classifiable according to the norms of IEC 60335 (IV editions) V-2: GWFI (>850°C) e GWIT (775°C) low halogen content, free from PBDE. Free from antimony and heavy metals in agreement to RoHS directive 2002/95/CE. This product offers a remarkable stability to light for exposure of long duration to sight on the outside, and a good compromise between tenacity and dimensional stability; available in the versions natural and colored as per sample. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.4 | % | |
| Flow | 1.4 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 30.0 | MPa | |
| Break, 23°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 7.0 | % | |
| Break, 23°C | 300 | % | |
| Flexural Modulus 1(23°C) | 1500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 1.8 | kJ/m² | |
| -20°C | 2.1 | kJ/m² | |
| 23°C | 5.0 | kJ/m² |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 6.3 | day | ISO 4577 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Needle Flame Test 2(2.00 mm) | Pass | IEC 60695-2-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 82.0 | °C | ISO 306/B50 |
| Ball Pressure Test | Pass | IEC 335 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index 3 | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 725 | °C | IEC 60695-2-13 |
| Oxygen Index 4 | 24 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 190 | °C | |
| Mold Temperature | 30.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Method A-B |
| 3 . | INDONEO |
| 4 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer PBT-11030-GF | Polylink Polymers (India) Ltd. | PBT | Polylink Polymer |
| SILVER® SA-3698 | Guangdong Silver Age Sci & Tech. Co., Ltd | TPE | SILVER® |
| TECHNO ABS F5451G30 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Elastron® V V201.A78.B | Elastron USA, Inc. | TPV | Elastron® V |
| Iupilon® EGW2010DR 9005 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |