Sorona® 3015G NC010
| Category: | PTT , RENEWABLY SOURCED™ THERMOPLASTIC POLYMER* |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Sorona® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WHcIG0_Sorona-3015G-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Glass Reinforced Polytrimethylene Terephthalate with Resin Made from Bio-PDO |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.20 | % | |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 125 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 5800 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 5.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 223 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Melting Temperature 1 | 227 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.5E-5 | cm/cm/°C | |
| Transverse | 8.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.70 | ||
| Dissipation Factor (100 Hz) | 1.5E-3 | IEC 60250 | |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 19 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.25 | g/cm³ |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE P5510 | SABIC Americas, Inc. | HDPE | SABIC® HDPE |
| Tenac™-C 7513 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Terblend® N NG-02EF | INEOS Styrolution Group GmbH | ABS+Nylon | Terblend® N |
| ASTALAC™ ABS M121 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| LNP™ LUBRICOMP™ BX02715 compound | SABIC Innovative Plastics | SAN | LNP™ LUBRICOMP™ |