SEPAZ™ HT61X10
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WHAgn9_SEPAZ-HT61X10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ HT61X10 is excellent heat resistance MPPO product. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 73.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 30 | % | ASTM D638 |
| Flexural Modulus 3 | 2700 | MPa | ASTM D790 |
| Flexural Strength 4 | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 49 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 165 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 270 - 300 | °C | |
| Front Temperature | 270 - 300 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 60.0 - 100 | °C |
| Injection instructions |
|---|
| Injection Speed: 30 to 70%Injection Pressure - 1st: 20 to 50%Injection Pressure - 2nd: 20 to 50%Injection Pressure - Back Pressure: 0 to 20% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Esterlloy™ AT900 | Asahi Kasei Chemicals Corporation | ABS Alloy | Esterlloy™ |
| ESPRENE EPDM 6101 | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| POLYfill PPH GF5030 PB | Polykemi AB | PP Homopolymer | POLYfill |
| Sylvin 8950-85 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ULTEM™ 1010M resin | SABIC Innovative Plastics | PEI | ULTEM™ |