Lupoy® RF3208F
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WGOETY_Lupoy-RF3208F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy®RF3208F is a polycarbonate (PC) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lupoy®The main features of the RF3208F are:
Lupoy®Typical application fields of RF3208F are: electrical/electronic applications |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 38 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 53.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 70 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2550 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 93.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 120 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Reflectance (550 nm) | 97 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Rear Temperature | 250 - 280 | °C | |
| Middle Temperature | 260 - 290 | °C | |
| Front Temperature | 260 - 290 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 45.0 - 80.0 | °C | |
| Back Pressure | 0.981 - 3.92 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW001LE | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| Hifax TRC 221X 1 | LyondellBasell Industries | PP Copolymer | Hifax |
| LIHAN® D9000 | Nanjing Lihan Chemical Co., Ltd. | Nylon 12 | LIHAN® |
| Karina CREPE PVC COMPOUND -E 601D22/ 15 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PB825G5 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |