Isocor™ 6105
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Shakespeare Monofilaments and Specialty Polymers |
| Trademark: | Isocor™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WGA0TG_Isocor-6105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Isocor™ 6105 is a medium viscosity PA-610. This resin is specifically suited for applications requiring low moisture absorption and greater dimensional stability. Isocor™ 6105 is also used in applications requiring improved abrasion resistance. This resin can be processed using conventional techniques. Typical applications for 6105 include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.07 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | -- | 1.4 | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 60.0 | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | 300 | % | ASTM D638 |
| Flexural Modulus | 2000 | 1300 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 48 | 200 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 175 | 160 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 66.1 | 60.0 | °C | ASTM D648 |
| Melting Temperature | 215 | -- | °C | DSC |
| Injection | Dry | Unit | |
|---|---|---|---|
| Dew Point | < -17.8 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Hopper Temperature | 79.4 | °C | |
| Rear Temperature | 221 - 243 | °C | |
| Middle Temperature | 227 - 260 | °C | |
| Front Temperature | 238 - 271 | °C | |
| Nozzle Temperature | 238 - 271 | °C | |
| Processing (Melt) Temp | 238 - 271 | °C | |
| Mold Temperature | 10.0 - 93.3 | °C | |
| Injection Pressure | 3.45 - 13.8 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 | MPa |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.10 | % | |
| Hopper Temperature | 79.4 | °C | |
| Cylinder Zone 1 Temp. | 254 | °C | |
| Cylinder Zone 2 Temp. | 266 | °C | |
| Cylinder Zone 3 Temp. | 271 | °C | |
| Cylinder Zone 4 Temp. | 271 | °C | |
| Die Temperature | 271 | °C |
| Extrusion instructions |
|---|
| Flange: 500°F (260°C)Air Dew Point (max): 0°F (-18°C)Neck: 500°F (260°C)Head: 480°F (250°C)Pump: 480°F (250°C)L/D Ratio: 24 to 30:1Compression Ratio: 3.5:1Polymer @ Die: 430°F (220°C)Screw Pressure: 2000 psi |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WACKER SilGel® 611 A/B | Wacker Chemie AG | Silicone | WACKER SilGel® |
| Zytel® HTN 52GM50EF WT001 | DuPont Performance Polymers | PPA | Zytel® HTN |
| Laramid G/30-V0HF1 | LATI S.p.A. | PPA | Laramid |
| Karina BLACK PVC COMPOUND 105900-48/ 1-B-ISE-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| O'Tech OW 125 XF | O'Tech Corporation | PVC, Unspecified | O'Tech |