LNP™ LUBRICOMP™ Lexan_LF1510A compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WG2EGu_LNPLUBRICOMPLexanLF1510Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% glass reinforced/15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.1 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.20 - 0.30 | % | Internal method |
| Transverse flow : 3.20mm | 0.35 - 0.50 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 72.4 | MPa | ASTM D638 |
| Fracture | 72.4 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 7.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 3790 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 510 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 16.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 133 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 127 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201 TFE 15 SI 2 | RTP Company | Nylon 66 | RTP |
| Texalan® 7 Series 764D | Austin Novel Materials Co. Ltd. | TPU Alloy | Texalan® 7 Series |
| WanBlend® WHT-THF9485T2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | WanBlend® |
| Infino NH-1015 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| MAJ'ECO FP374HGB | AD majoris | PP, Unspecified | MAJ'ECO |