TOTAL Polyethylene HDPE D4720 Datasheet,HDPE, MMW,TOTAL Refining & Chemicals-SHANGHAI SUSHENG

Message
HDPE 4720 Polyethylene: Medium Molecular Weight High Density Film Resin Characteristics Excellent processability Good tear and impact strength Good stiffness Excellent compatibility with LDPE and LLDPE Excellent drawdown Good moisture barrier properties Applications Multi-wall liner Gas flush poultry bags Mailing envelopes Heavy-duty shipping sacks Fresh cut produce packaging Coextrusions

General Information
Features	Good Drawdown Good Impact Resistance Good Processability Good Tear Strength High Density High Stiffness Medium Molecular Weight Moisture Resistant
Uses	Bags Food Packaging Heavy-duty Bags Liners Packaging
Processing Method	Blown Film Coextrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.947	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)			ASTM D1238
190°C/2.16 kg	0.28	g/10 min
190°C/21.6 kg	20	g/10 min

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
Secant Modulus ¹			ASTM D882A
1% Secant, MD : 25 µm	710	MPa
1% Secant, TD : 25 µm	1000	MPa
Tensile Strength			ASTM D882A
MD : Yield, 25 µm ²	24.1	MPa
MD : Yield, 25 µm ³	23.4	MPa
TD : Yield, 25 µm ⁴	25.5	MPa
TD : Yield, 25 µm ⁵	26.2	MPa
MD : Break, 25 µm ⁶	4.83	MPa
MD : Break, 25 µm ⁷	62.1	MPa
TD : Break, 25 µm ⁸	39.3	MPa
TD : Break, 25 µm ⁹	18.6	MPa
Tensile Elongation			ASTM D882A
MD : Break, 25 µm ¹⁰	600	%
MD : Break, 25 µm ¹¹	450	%
TD : Break, 25 µm ¹²	700	%
TD : Break, 25 µm ¹³	600	%
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm ¹⁴	28	g
MD : 25 µm ¹⁵	10	g
TD : 25 µm ¹⁶	530	g
TD : 25 µm ¹⁷	1500	g
Water Vapor Transmission Rate ¹⁸(38°C, 25 µm)	7.8	g/m²/24 hr	ASTM E96

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	131	°C	ASTM D3417

Additional Information	Nominal Value	Unit	Test Method
Dart Impact			ASTM D1709
25.4 µm ¹⁹	100	g
25.4 µm ²⁰	< 50	g

Extrusion	Nominal Value	Unit
Melt Temperature	193 to 216	°C

Note Message
1 .	Film was produced at 1.0 mil with a 2.5 BUR
2 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
3 .	Film was produced at 1.0 mil with a 2.5 BUR
4 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
5 .	Film was produced at 1.0 mil with a 2.5 BUR
6 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
7 .	Film was produced at 1.0 mil with a 2.5 BUR
8 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
9 .	Film was produced at 1.0 mil with a 2.5 BUR
10 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
11 .	Film was produced at 1.0 mil with a 2.5 BUR
12 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
13 .	Film was produced at 1.0 mil with a 2.5 BUR
14 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
15 .	Film was produced at 1.0 mil with a 2.5 BUR
16 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
17 .	Film was produced at 1.0 mil with a 2.5 BUR
18 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
19 .	High Stalk Extrusion - Film was produced at 1.0 mil with a 6:1 FLH/D ratio and a 4:1 BUR
20 .	Film was produced at 1.0 mil with a 2.5 BUR

Category:	HDPE, MMW , High Density (MMW) Polyethylene
Manufacturer:	TOTAL Refining & Chemicals
Trademark:	TOTAL Polyethylene
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	WFHYYb_TOTAL-Polyethylene-HDPE-D4720.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SAPYLENE T25GF15HB	Sahel Chimie Co.	PP, Unspecified	SAPYLENE
Sunny® PA66 EN400	Guangdong Shunde Shunyan New Material Co., Ltd.	Nylon 66	Sunny®
Zhongfa AS AS-G	Yuyao Zhongfa Engineering Plastics Co. Ltd.	AS	Zhongfa
EPLAMID 6 CFR 10 NC	EPSAN Plastik SAN. ve TiC. A.S.	Nylon 6	EPLAMID 6
Hostacom TRC 333N D82659	LyondellBasell Industries	PP Copolymer	Hostacom