Next Nylon 66 Prime Series PGF25-01BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WF9hFv_Next-Nylon-66-Prime-Series-PGF25-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced FR Black Compound Product Applications This Red Phosphorous Flame retardant grades provides robust UL-94 V0 and a full UL Yellow card. This grade is suitable for molding insulating parts for electrical devices, and more generally for a thin parts under stress. Benefits High Mechanical Properties, Low optical density of smokes, Excellent Filling qualities |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.38 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.50 | -- | % | ASTM D955 |
| Transverse flow | 0.90 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.75 | -- | % | ASTM D570 |
| Saturation 1 | 6.4 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 105 | -- | ASTM D785 | |
| Class r | 125 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 130 | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 7500 | 600 | MPa | ASTM D790 |
| Flexural Strength | 210 | 140 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 83 | 98 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 260 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 250 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 26 | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applicationsPossible Formation of Phosphates in Humid warm environments |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 270 - 275 | °C | |
| Middle Temperature | 275 - 280 | °C | |
| Front Temperature | 275 - 280 | °C | |
| Mold Temperature | 70.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y200L (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Cellophane™ K160HB20/23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Delrin® 500P BK602 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Fainplast PVC KL 84/1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Mafill® CR CT 5344 | Ravago Group | PP Copolymer | Mafill® |