NatureFlex™ NE White
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | NatureFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WEaOSQ_NatureFlex-NE-White.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NatureFlex™ NE White is a Regenerated Cellulose product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Film. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Test Method | |
|---|---|---|---|
| Density - Optical | 0.300 | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Gauge | 23.1 | µm | Internal Method |
| Yield (23.1 µm) | 29.9 | m²/kg | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction 1(vs. Itself - Dynamic) | 0.30 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 23 µm | > 3000 | MPa | |
| 1% Secant, TD : 23 µm | > 1520 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 23 µm | 124 | MPa | |
| TD : Yield, 23 µm | 68.9 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 23 µm | 22 | % | |
| TD : Break, 23 µm | 70 | % | |
| Seal Strength 2 | 0.15 | N/mm | Internal Method |
| Seal Initiation Temperature (23 µm) | 79.4 to 199 | °C | Internal Method |
| Oxygen Transmission Rate (Wet) (24°C, 23 µm, 0.0% RH) | 3.10 | cm³/m²/24 hr | ASTM F1927 |
| Water Vapor Transmission 3 | 31 | g/m²/24 hr | ASTM E96 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°, 23.1 µm) | 55 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | Thickness: 0.91 mil |
| 2 . | Thickness: 0.91 mil |
| 3 . | 100°F, 90%RH, thickness: 0.91 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9302-75FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Torelina® A575W20 | Toray Resin Company | PPS | Torelina® |
| COPYLENE® CR350CL-01 | Phillips 66 | PP Random Copolymer | COPYLENE® |
| Jampilen EP548R | Jam Polypropylene Company | PP Copolymer | Jampilen |
| Karina BLACK PVC COMPOUND 951-48/4-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |