GLS PC MG49
| Category: | PC , Polycarbonate |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WEFVaD_GLS-PC-MG49.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC 20 GF Precolor |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 to 1.43 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | > 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | > 5000 | MPa | ASTM D638 |
| Tensile Strength 1(Yield) | > 90.0 | MPa | ASTM D638 |
| Flexural Modulus | > 5000 | MPa | ASTM D790 |
| Flexural Strength | > 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 139 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 85.0 to 122 | °C | |
| Injection Pressure | 68.0 to 104 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP562 | Southern Polymer, Inc. | LDPE | PRIMALENE |
| ADDILENE PMD 50218 | ADDIPLAST | PP, Unspecified | ADDILENE |
| Geon™ Vinyl Flexible R3792C | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Iupilon® GSH2030R2 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LubriOne™ AT-000/10T | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |