Jackdaw PLA HT16WT6652
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Jackdaw PLA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WD61bI_Jackdaw-PLA-HT16WT6652.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jackdaw PLA HT16WT6652 is a Polylactic Acid (PLA) product. It is available in Europe. Primary characteristic: eco-friendly/green. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (170°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5900 | MPa | ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 40.0 | MPa | |
| Break | 39.0 | MPa | |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 1.0 | % | |
| Break | 1.5 | % | |
| Flexural Modulus | 4700 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 50.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 1 | 8.50 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 8.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 50.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 148 | °C | ISO 1218, ASTM D2117 |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miflon® 3213 | Jiangsu Meilan Chemical Co., Ltd. | PTFE | Miflon® |
| NOVADURAN® 5010G30 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Axiall PVC 11441 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Clariant Nylon 6/6 PA-133 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Kepital® F25-03H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |