Durethan® BCF 30 X H2.0 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WCoX4W_Durethan-BCF-30-X-H2-0-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers/carbon fibers, injection molding, heat-aging stabilized, improvedElectrical conductivity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.33 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 15.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Across Flow : 280°C, 2.00 mm 1 | 0.77 | -- | % | ISO 294-4 |
| Across Flow : 120°C, 2 hr, 2.00 mm 2 | 0.080 | -- | % | ISO 294-4 |
| Flow : 280°C, 2.00 mm 3 | 0.22 | -- | % | ISO 294-4 |
| Flow : 120°C, 2 hr, 2.00 mm 4 | 0.030 | -- | % | ISO 294-4 |
| Across Flow : 23°C, 3.00 mm 5 | 0.75 | -- | % | ISO 2577 |
| Across Flow : 120°C, 2 hr, 3.00 mm 6 | 0.10 | -- | % | ISO 294-4 |
| Flow : 280°C, 3.00 mm 7 | 0.15 | -- | % | ISO 2577 |
| Flow : 120°C, 2 hr, 3.00 mm 8 | 0.030 | -- | % | ISO 2577 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 13500 | 6700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 185 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.9 | 5.0 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 3.5 | -- | % | ISO 527-2/50 |
| Flexural Modulus 9(23°C) | 11500 | 6800 | MPa | ISO 178/A |
| Flexural Stress 10 | ||||
| 3.5% Strain | -- | 145 | MPa | ISO 178/A |
| 23°C | 280 | 160 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 11(23°C) | 3.5 | 5.0 | % |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electrical Resistivity | 40 | -- | ohms·cm | ISO 3915 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 12(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-140, (GF+CF) 30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 13 | 1.70 | -- | J | |
| -- 14 | 2.40 | -- | J |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | -- | kJ/m² | |
| 23°C | 11 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 60 | kJ/m² | |
| 23°C | 75 | 80 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 10 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 60 | 60 | kJ/m² | |
| 23°C | 65 | 65 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 219 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 140 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | 214 | -- | °C | ISO 306/B120 |
| Melting Temperature 15 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 150 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 150x150x3 |
| 6 . | 150x150x3 |
| 7 . | 150x150x3; MT 80°C; 500 Bar |
| 8 . | 150x150x3 |
| 9 . | 2.0 mm/min |
| 10 . | 2.0 mm/min |
| 11 . | Pull Rate: 2 mm/min; 50% RH |
| 12 . | US-FMVSS302 |
| 13 . | -30°C |
| 14 . | 23°C |
| 15 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 53 G 10-1 | Ravago Group | PP Homopolymer | Scolefin |
| SLOVALEN® PH 69 GF 25 | Plastcom | PP, Unspecified | SLOVALEN® |
| APEX® RE 8103R-NT | Teknor Apex Company | PVC, Rigid | APEX® |
| LNP™ LUBRICOMP™ RFN16 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| Wuxi Jiahong EB-208XX | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |