Adflex X 101 H
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WCkS1x_Adflex-X-101-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex X 101 H is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell's proprietary Catalloy process technology. It exhibits a high softness and a low modulus, with a relatively high melt flow index. Adflex X 101 H is tailored to replace atactic polypropylene copolymers (APP) used for the modification of bitumen in roofing membranes. The percentage to be added can vary according to the quantity of the atactic polypropylene used in combination with Adflex X 101 H and the requested cold bending temperature of the end product. Due to the high molecular weight of Adflex X 101 H, high blend viscosity and good penetration values are obtained. Its structure is tailored to obtain easy dispersion and phase inversion in the bitumen blend. Adflex X101H is also used in other industrial applications where high flexibility and the capability of accepting high filler loading levels are required. The grade is available in natural pellet form. For regulatory compliance information see Adflex X 101 H Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1(48 hr, 3.20 mm) | 1.0 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 30 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 6.00 | MPa | |
| Break | 10.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | > 40 | % | |
| Break | > 800 | % | |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 67.0 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.0 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 36.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 55.0 | °C | ISO 306/A50 |
| Note Message | |
|---|---|
| 1 . | 100x150x3.2 mm |
| 2 . | Die C, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 C SI 2 | RTP Company | PPS | RTP |
| Latamid 66 B G/20-V | LATI S.p.A. | Nylon 66 | Latamid |
| Karina WHITE PVC COMPOUND -E500-10/1-BT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OnFlex™ S KE 60A-3S1725 | PolyOne Corporation | TPE | OnFlex™ |
| LNP™ THERMOCOMP™ 5C004 compound | SABIC Innovative Plastics | PVDF | LNP™ THERMOCOMP™ |