Terluran® GP-35
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terluran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WCaGfK_Terluran-GP-35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terluran GP-35 is high-flow, general purpose injection molding grade with good ductility, intended for moldings with thin walls and/or adverse flow length to wall ratio. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 3.1 | g/10 min | |
| 220°C/10.0 kg | 34 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | |||
| 230°C/3.8 kg | 11.0 | cm³/10min | ASTM D1238 |
| 220°C/10.0 kg | 34.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 to 0.70 | % | ASTM D955 |
| -- | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation, 23°C | 0.95 | % | ASTM D570, ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.24 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 | |
| Ball Indentation Hardness | 99.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 2500 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 45.0 | MPa | ASTM D638 |
| Yield, 23°C | 44.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 2.4 | % | ISO 527-2 |
| Break | 2.4 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 12 | % | ISO 527-2 |
| Flexural Modulus | 2350 | MPa | ASTM D790 |
| Flexural Strength | 65.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 19 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 90 | kJ/m² | |
| 23°C | 130 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 80 | J/m | ASTM D256 |
| -18°C | 85 | J/m | ASTM D256 |
| 23°C | 240 | J/m | ASTM D256 |
| -30°C | 7.0 | kJ/m² | ISO 180/A |
| 23°C | 22 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 88.9 | °C | ASTM D648 |
| 0.45 MPa, Annealed | 101 | °C | ASTM D648 |
| 0.45 MPa, Annealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 96.7 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 92.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 102 | °C | ISO 306/A50 |
| -- | 95.0 | °C | ISO 306/B50 |
| CLTE - Flow | 8.0E-5 to 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant (1.00 mm, 1 MHz) | 2.80 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 15 | YI | DIN 6167 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MFE® -30 | Huachang Polymer Co., Ltd. | Vinyl Ester | MFE® |
| TECHNYL® A 50H1 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| UMG WOOD® W310AM | UMG ABS, Ltd. | ASA | UMG WOOD® |
| Glastic® UTS 1478 | Glastic Corporation | Polyester, TS | Glastic® |
| EPAMOULD 265D12 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |