ULTEM™ HU2100 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WCEGTS_ULTEMHU2100resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocompatible (ISO 10993 or USP Class VI). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/3.8 kg) | 5.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4680 | MPa | ASTM D638 |
| -- | 4500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 114 | MPa | ASTM D638 |
| Yield | 115 | MPa | ISO 527-2/5 |
| Fracture 3 | 115 | MPa | ASTM D638 |
| Fracture | 115 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/5 |
| Fracture 5 | 6.0 | % | ASTM D638 |
| Fracture | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 5500 | MPa | ASTM D790 |
| -- 7 | 4500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 185 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 53 | J/m | ASTM D256 |
| 23°C | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength 10 | ISO 180/1U | ||
| -30°C | 30 | kJ/m² | ISO 180/1U |
| 23°C | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 10.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 205 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 11 | 205 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 223 | °C | ASTM D1525 12 |
| -- | 212 | °C | ISO 306/B50 |
| -- | 217 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 3.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 23 to 150°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI | 170 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 15 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 120 | °C | |
| Rear Temperature | 340 - 395 | °C | |
| Middle Temperature | 350 - 405 | °C | |
| Front Temperature | 360 - 415 | °C | |
| Nozzle Temperature | 350 - 405 | °C | |
| Processing (Melt) Temp | 370 - 410 | °C | |
| Mold Temperature | 140 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 120*10*4 mm |
| 12 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PS 3124 70/42 | MBA Polymers | PS (GPPS) | MBA PS |
| Prime Polypro™ J226T | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| Unichem 7011LT-03 | Colorite Polymers | PVC, Unspecified | Unichem |
| DENILUB PBT NEAT RESIN | Vamp Tech | PBT | DENILUB |
| Polifor® E 12 TR/10 NERO | SO.F.TER. SPA | PP Copolymer | Polifor® |