RX® 613
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | RX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WCDqhA_RX-613.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RX® 613 is a fiberglass reinforced phenolic molding compound, with good dimensional stability and good strength at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.60 | g/cm³ | ISO 1183 |
| Apparent Density | 0.75 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.25 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Compression Molded) | 85.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 14000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 175 | MPa | ISO 178 |
| Compressive Stress | 350 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (Compression Molded) | 3.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 185 | °C | |
| 1.8 MPa, Annealed | > 282 | °C | |
| CLTE - Flow | 1.8E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.41 | W/m/K | ASTM C518 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI Str | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 14 | kV/mm | ASTM D149 |
| Arc Resistance | 150 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® S-1150 | Lubrizol Advanced Materials, Inc. | ABS | Stat-Rite® |
| Sylvin 5132-86 Clear Orange 585 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 4215-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ GFN2 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Moplen EP300H | LyondellBasell Industries | PP Impact Copolymer | Moplen |