Dow Corning® C6-180

Category:	Silicone , Silicone
Manufacturer:	Dow Corning Corporation
Trademark:	Dow Corning®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	WBwB5P_DowCorningC6180.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
High Consistency Rubber silicone elastomers for device and component fabrication in the healthcare industry. APPLICATIONS DOW CORNING Class VI Elastomers (C6-135, C6-150, C6-165, C6-180) Parts A & B are platinum-catalyzed heat-cure silicone High Consistency Rubbers for part fabrication, extrusion and medical devices, including those intended for implantation in humans for up to 29 days. DESCRIPTION DOW CORNING Class VI Elastomers (C6-135, C6-150, C6-165, C6-180) Parts A & B are a series of two-part platinum-catalyzed silicone elastomers. Each elastomer is supplied as a two-part kit (Part A & Part B), equal portions of which must be thoroughly blended together prior to use. The elastomer is thermally cured via an addition-cure (platinum-catalyzed) reaction. When blended and cured as indicated, the resulting elastomer consists of crosslinked dimethyl and methyl-vinyl siloxane copolymers and reinforcing silica. The elastomers are available in a range of nominal hardness from 35 to 80, durometer, Shore A. The elastomers can normally be used without any post-cure, although if necessary, this may be employed to stabilize final properties. Furthermore, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

Message

High Consistency Rubber silicone elastomers for device and component fabrication in the healthcare industry.

APPLICATIONS
DOW CORNING Class VI Elastomers (C6-135, C6-150, C6-165, C6-180) Parts A & B are platinum-catalyzed heat-cure silicone High Consistency Rubbers for part fabrication, extrusion and medical devices, including those intended for implantation in humans for up to 29 days.

DESCRIPTION
DOW CORNING Class VI Elastomers (C6-135, C6-150, C6-165, C6-180) Parts A & B are a series of two-part platinum-catalyzed silicone elastomers. Each elastomer is supplied as a two-part kit (Part A & Part B), equal portions of which must be thoroughly blended together prior to use.
The elastomer is thermally cured via an addition-cure (platinum-catalyzed) reaction. When blended and cured as indicated, the resulting elastomer consists of crosslinked dimethyl and methyl-vinyl siloxane copolymers and reinforcing silica.

The elastomers are available in a range of nominal hardness from 35 to 80, durometer, Shore A. The elastomers can normally be used without any post-cure, although if necessary, this may be employed to stabilize final properties. Furthermore, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

General Information
Features	High Gas Permeability No frost Good coloring High pressure heating resistance
Uses	Medical/nursing supplies
Agency Ratings	ISO 10993-Part I USP Class VI
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	1.8	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	77		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (200% Strain)	3.68	MPa	ASTM D412
Tensile Strength	7.23	MPa	ASTM D412
Tensile Elongation (Break)	610	%	ASTM D412
Tear Strength ¹	39.1	kN/m	ASTM D624

Note Message
1 .	B mould

Resin Grade	Manufacturer	Category	Trademark
Varcum 29335	Durez Corporation	Phenolic	Varcum
KEBAFORM® C 901 SO	BARLOG plastics GmbH	Acetal (POM) Copolymer	KEBAFORM® C
Lucel® GC210	LG Chem Ltd.	Acetal (POM) Copolymer	Lucel®
Sylvin 5170-85 Yellow 405	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
API II 370	API II, Inc.	PS (GPPS)	API II