ICORENE® N1016
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | ICO Polymers EMEA, A Division of A. Schulman |
| Trademark: | ICORENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WBgTrx_ICORENE-N1016.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ICORENE® N1016 is a premium copolymer of ethylene vinyl acetate specifically designed for the preparation of masterbatch and textile bonding. The powder form can achieve better colour developments or additive dispersion in a masterbatch than the pellet form. The vinyl acetate content is about 28 %. Maximum processing tem- perature 200°C. ICORENE® N1016 can be used in various applications such as hot melt adhesives. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 150 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 28.0 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | < 200 | °C | |
| Peak Melting Temperature | 66.0 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SORVEX 500 | Sorensen Ventures | PBT | SORVEX |
| Ultramid® A3HG5 BK00564 | BASF Corporation | Nylon 66 | Ultramid® |
| Nucrel® 30705 | DuPont Packaging & Industrial Polymers | EAA | Nucrel® |
| ELIX™ ABS M406 | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Halene H E5201 | Haldia Petrochemicals Ltd. | HDPE | Halene H |