Latigloss 66 H2 G/50-V0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigloss |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WAngQP_Latigloss-66-H2-G-50-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 66 (PA 66). Heat stabilised. Glass fibres. UL94 V-0 classified, with halogens, PBB/PBDE free. PHYSICAL PROPERTIES - Typical values STANDARD |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.83 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.55 to 0.80 | % | |
| Flow : 2.00 mm | 0.25 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 22000 | MPa | |
| 60°C | 15500 | MPa | |
| 90°C | 10000 | MPa | |
| 120°C | 7800 | MPa | |
| 150°C | 6000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 210 | MPa | |
| Break, 60°C | 170 | MPa | |
| Break, 90°C | 135 | MPa | |
| Break, 120°C | 115 | MPa | |
| Break, 150°C | 100 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.8 | % | |
| Break, 60°C | 3.0 | % | |
| Break, 90°C | 3.5 | % | |
| Break, 120°C | 3.8 | % | |
| Break, 150°C | 4.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | °C | |
| Vicat Softening Temperature | 250 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 90.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unipren® Elastomers A3 CRLA010 45A EB05IN1 UP358 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Geon™ Vinyl Flexible B87FB | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Kingfa PA66-ROW | Kingfa | Nylon 66 | Kingfa |
| KPOL-PP K-PPH 8.5F | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| Sylvin 8389-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |