Chemlon® 60GS8H Datasheet,Nylon 6,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
60GS8H is a 40% glass sphere filled, heat stabilised nylon 6 that offers excellent rigidity coupled with minimal distortion.

General Information
Filler / Reinforcement	Glass beads, 30% filler by weight
Additive	heat stabilizer
Features	Rigidity, high Thermal Stability
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.45	g/cm³	ISO 1183
Molding Shrinkage ¹	0.60 - 1.5	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	1.0	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4800	MPa	ISO 527-2
Tensile Stress (Break)	88.0	MPa	ISO 527-2
Tensile Strain (Break)	4.0	%	ISO 527-2
Flexural Modulus	4500	MPa	ISO 178
Flexural Stress ²	125	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	6.0	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	32	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 200	°C	ISO 75-2/B
1.8 MPa, not annealed	90.0	°C	ISO 75-2/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	IEC 60093
Volume Resistivity	1.0E+17	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	10	kV/mm	IEC 60243-1
Relative Permittivity	3.80		IEC 60250
Dissipation Factor (1 MHz)	0.020		IEC 60250
Comparative Tracking Index	525	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	22	%	ISO 4589-2

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Rear Temperature	240 - 290	°C
Middle Temperature	240 - 290	°C
Front Temperature	240 - 290	°C
Processing (Melt) Temp	< 300	°C
Mold Temperature	60.0 - 80.0	°C
Injection Rate	Fast
Screw Speed	50 - 200	rpm

Injection instructions
背压：低注射压力：高如果材料在空气中暴露的时间不超过3小时，则无需干燥。

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The single point values stated were determined from a shallow box moulding of 50 x 50 x 10mm, with 2mm general wall thickness and internal ribbing of 1.5mm thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).
2 .	At Break

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The single point values stated were determined from a shallow box moulding of 50 x 50 x 10mm, with 2mm general wall thickness and internal ribbing of 1.5mm thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

2 .

At Break

Resin Grade	Manufacturer	Category	Trademark
TECHNYL® A 218G1 V30 BLACK 34 N	Solvay Engineering Plastics	Nylon 66	TECHNYL® A
Moldex® QS262D/QCM240	Mitsubishi Chemical Corporation	Polyolefin, Unspecified	Moldex®
EPLAMID 66 GV0 30 NC	EPSAN Plastik SAN. ve TiC. A.S.	Nylon 66	EPLAMID 66
Hostacom HKG 126D NAT	LyondellBasell Industries	PP Homopolymer	Hostacom
LNP™ STAT-KON™ MFD03 compound	SABIC Innovative Plastics	PP, Unspecified	LNP™ STAT-KON™

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	WAPnx1_Chemlon-60GS8H.pdf
PRICE:	Order Products email sales@su-jiao.com