INSULCAST® LN 1-05
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WAOAW1_INSULCAST-LN-1-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST LN 1-05 is a non-cracking epoxy compound that was specifically designed for large potting and encapsulation applications. It displays excellent electrical properties over a wide range of temperatures. INSULCAST LN 1-05 makes use of the latest polymer and filler technology. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 72.0 to 78.0 | °C | |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.65 | W/m/K | |
| Service Temperature | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.010 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Volume: 4.2 Mix Ratio by Weight: 7.2 | ||
| Part B | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 1.0 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Black | ||
| -- 2 | Colorless | ||
| Density | |||
| -- 3 | 0.938 | g/cm³ | |
| -- 4 | 1.62 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| 25°C 5 | 0.010 | Pa·s | |
| -- 6 | 5.0 | Pa·s | |
| 25°C 7 | 120 | Pa·s | |
| Curing Time | |||
| -- 8 | 18 | hr | |
| 25°C | 36 | hr | |
| Pot Life (25°C) | 480 to 600 | min |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | Mixed |
| 7 . | Part A |
| 8 . | 16 hours at 25°C followed by 2 hours at 65°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPLUB K 00U 2 TF | Vamp Tech | PEEK | VAMPLUB |
| Amilan® CM2006 | Toray Resin Company | Nylon 610 | Amilan® |
| Estane® 5714 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Keltan® 6950C | LANXESS Buna GmbH | EPDM | Keltan® |
| PEARLSTICK® D40-70/03 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLSTICK® |