TOTAL Polyethylene HDPE 2285
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W8ogTS_TOTAL-Polyethylene-HDPE-2285.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TOTAL Polyethylene 2285 is a High Density (HMW) Polyethylene material. It is available in North America for film extrusion. Important attributes of TOTAL Polyethylene 2285 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.951 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | |
| 190°C/21.6 kg | 11 | g/10 min | |
| 190°C/5.0 kg | 0.32 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Secant Modulus 1 | ASTM D882A | ||
| 2% Secant, MD : 20 µm, Blown Film | 841 | MPa | |
| 2% Secant, TD : 20 µm, Blown Film | 910 | MPa | |
| Tensile Strength 2 | ASTM D882A | ||
| MD : Yield, 20 µm, Blown Film | 36.5 | MPa | |
| TD : Yield, 20 µm, Blown Film | 34.5 | MPa | |
| MD : Break, 20 µm, Blown Film | 63.4 | MPa | |
| TD : Break, 20 µm, Blown Film | 67.6 | MPa | |
| Tensile Elongation 3 | ASTM D882A | ||
| MD : Break, 20 µm, Blown Film | 300 to 500 | % | |
| TD : Break, 20 µm, Blown Film | 300 to 500 | % | |
| Dart Drop Impact (20 µm, Blown Film) | 350 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm, Blown Film | 24 | g | |
| TD : 20 µm, Blown Film | 120 | g | |
| Water Vapor Transmission Rate (38°C, 20 µm, Blown Film) | 12 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 132 | °C | ASTM D3417 |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® Rx1452 | Covestro - Polycarbonates | PC | Makrolon® |
| TECHNYL® A 218 V25 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| TAIRILAC AF3500 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Fainplast PVC PHT 0144 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| LOXIM 820 01 HBCC | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |