Order Products : sales@su-jiao.com
Zytel® FR7025V0F NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W8nX1g_ZytelFR7025V0FNC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, Flame Retardant, Non-Halogenated, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.0 | % | ISO 294-4 |
| Flow | 0.90 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.8 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3750 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 3660 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 3.0 | kJ/m² | ISO 179/1eA |
| -30°C | 3.0 | kJ/m² | ISO 179/1eA |
| 23°C | 3.7 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 140 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 84.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 31 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.75 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| Oxygen Index | 35 | % | ISO 4589-2 |
| FMVSS Flammability | B | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 280 | °C | |
| Mold Temperature, Optimum | 70 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Ejection Temperature | 210 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S HSK 305 M NER (21038) | Radici Plastics | Nylon 6 | Radilon® |
| Quadraflex™ ARE-55D | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Wellamid® GFT33N051-NBK2 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Globalprene® 3411P | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Karina RED COLOR CONCNETRATE 42/155-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |