Badamid® LB70 GF35
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W7xcRm_Badamid-LB70-GF35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® LB70 GF35 is a Polyamide 6 (Nylon 6) material filled with 35% glass fiber. It is available in Europe. Primary attribute of Badamid® LB70 GF35: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10500 | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 190 | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.5 | 8.0 | % | ISO 527-2/5 |
| Flexural Stress (23°C) | 190 | 120 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 15 | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 85 | -- | kJ/m² | |
| 23°C | 95 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 222 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 1.5E-5 to 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 to 7.0E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 60216 | |||
| -- 2 | 135 | -- | °C | |
| -- | 200 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.80 | 6.30 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.021 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| 2 . | 20000 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoflon® T 538 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| Nypol® PA A3 G33 HS UV PRTA011 NR351 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Daelim Po1y® LD-05 | DAELIM INDUSTRIAL CO., LTD. | LDPE | Daelim Po1y® |
| LNP™ THERMOCOMP™ 9X94104 compound | SABIC Innovative Plastics Europe | PEI | LNP™ THERMOCOMP™ |
| LUVOCOM® 6-7834 VP | Lehmann & Voss & Co. | Nylon 12 | LUVOCOM® |