HONES® PA66 G25
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Guangdong Shunde Hones Polymer Material Co., Ltd. |
| Trademark: | HONES® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W72lwr_HONES-PA66-G25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Technology characteristics: 25% Glass fiber reinforced, heat-resistant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 125 | MPa | ASTM D638 |
| Flexural Strength | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 70 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 248 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 30 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.10 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 220 to 265 | °C | |
| Middle Temperature | 220 to 265 | °C | |
| Front Temperature | 220 to 265 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH 731E | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| VALOX™ 855 resin | SABIC Innovative Plastics | PBT | VALOX™ |
| Fortron® 1140L4 | Celanese Corporation | PPS | Fortron® |
| Karina WHITE PVC COMPOUND 851-10/127-Y-ERYB-AS-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OXPEKK® MG210C | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |