Arnitel® CM622
| Category: | TPC-ES , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnitel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W6WwYH_Arnitel-CM622.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arnitel® CM622 is a Thermoplastic Copolyester Elastomer (TPC-ES) material. It is available in Asia Pacific, Europe, or North America for extrusion. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 310 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 33.0 | MPa | |
| 5.0% Strain | 14.5 | MPa | |
| 10% Strain | 19.8 | MPa | |
| 50% Strain | 22.0 | MPa | |
| 100% Strain | 20.4 | MPa | |
| Nominal Tensile Strain at Break | 590 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 190 | °C | ISO 306/A50 |
| -- | 87.0 | °C | ISO 306/B50 |
| Melting Temperature 1 | 208 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 208K BLACK 10N-L | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| ASACLEAN™ GL2 | ASACLEAN - Sun Plastech Inc. | Proprietary | ASACLEAN™ |
| Celcon® M270™ | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Infino VB-5300GS | SAMSUNG SDI CO., LTD. | PBT | Infino |
| LNP™ LUBRICOMP™ DL002P compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |