LEXAN™ EM3110 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W6Coxg_LEXAN-EM3110-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Automotive interiors. Optimizes flow/processability for cost effective thinner wall design uses. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.16 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 57.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 110 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 2030 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 81.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 210 | J/m | |
| -20°C | 590 | J/m | |
| 23°C | 640 | J/m | |
| 23°C, 6.40 mm | 210 | J/m | |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 56.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 127 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 118 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 124 | °C | |
| CLTE - Flow (-40 to 95°C) | 6.5E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 254 to 277 | °C | |
| Middle Temperature | 266 to 288 | °C | |
| Front Temperature | 277 to 299 | °C | |
| Nozzle Temperature | 271 to 293 | °C | |
| Processing (Melt) Temp | 277 to 299 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVA PC 2000 | NOVA Polymers, Inc. | PC | NOVA PC |
| ChronoPrene™ 25A | CardioTech International, Inc. | TPE | ChronoPrene™ |
| CP PRYME® Polypropylene PPC100RC-35M | Chase Plastics Services Inc. | PP Random Copolymer | CP PRYME® Polypropylene |
| ELASTOSIL® LR 3844/20 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| 3M™ Dyneon™ PTFE Compound TF 8637 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |