Celanex® 2402 MT
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W5sGBA_Celanex-2402-MT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 2402 MT Natural is an unreinforced PBT with improved flow that complies with the requirements of CFR 21 177.1660 of the Food and Drug Administration (FDA) and is listed in the Drug Master File (DMF) 10047 (US) / 10033 (EU) and the Device Master File (MAF) 443 (US) / 1078 (EU).. 2402 MT also complies with the corresponding EU and national registry regulatory requirements. 2402 MT has displayed excellent biocompatibility in tests corresponding to USP 23 class VI. Celanex 2402 MT contains no animal derived materials. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 1.8 - 2.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 15 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2550 | MPa | ISO 178 |
| Flexural Stress (23°C) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.5 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 130 | kJ/m² | ISO 179/1eU |
| 23°C | 140 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 190 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3 |
| CLTE - Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Beetafin® RV9020 | BIP (Oldbury) Limited | PUR-Ester | Beetafin® |
| Alpha PVC GW 2462-H VW1 NAT LCF | AlphaGary | PVC, Semi-Rigid | Alpha PVC |
| Honeywell PCTFE P10000HS | Honeywell | PCTFE | Honeywell PCTFE |
| Ipethene® 213 | Carmel Olefins Ltd. | LDPE | Ipethene® |
| Karina ORANGE COLOR CONCNETRATE 32/ 82-FC-(CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |