TECHNYL STAR™ AFX 218 V50 BLACK 31N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL STAR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W5eVx1_TECHNYL-STAR-AFX-218-V50-BLACK-31N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYLSTAR™ AFX 218 V50 Black 31N is based on a patented high flow polyamide 66 resin (Technylstar), heat stabilized, reinforced with 50% of glass fibre, for injection moulding. It is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.42 | -- | % | |
| Flow | 0.34 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.60 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17000 | 12500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 255 | 180 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.5 | 3.5 | % | ISO 527-2/1A |
| Flexural Modulus | 15000 | -- | MPa | ISO 178 |
| Flexural Stress | 380 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 21 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 100 | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 17 | 21 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 88 | 91 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 256 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 264 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 675 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DIOSHY® MP-845 | DIOSHY Co.,Ltd. | SBS | DIOSHY® |
| Kingfa JH830 | Kingfa | PC Alloy | Kingfa |
| LNP™ STAT-KON™ ZE0039 compound | SABIC Innovative Plastics | PPE+PS | LNP™ STAT-KON™ |
| MAJORIS AFR081 | AD majoris | PP Copolymer | MAJORIS |
| Sylvin 4200-75FUV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |