LNP™ THERMOCOMP™ ZF004 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W5Oc1F_LNP-THERMOCOMP-ZF004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP ZF004 is a compound based on PPO resin containing 20% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound ZF-1004 Product reorder name: ZF004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6570 | MPa | ASTM D638 |
| -- | 6510 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 80.1 | MPa | ASTM D638 |
| Break | 79.4 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.9 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 6410 | MPa | ASTM D790 |
| -- 5 | 6270 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 121 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 70 | J/m | ASTM D256 |
| 23°C 7 | 8.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 390 | J/m | ASTM D4812 |
| 23°C 8 | 31 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 12.5 | J | ASTM D3763 |
| -- | 2.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 137 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 131 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 131 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalite R540M | Spartech Plastics | ABS+PVC | Royalite |
| RR Advantage R-COPP 12 | Resin Resource, Inc. | PP Random Copolymer | RR Advantage |
| Witcom POM-C 4L3 | Witcom Engineering Plastics B.V. | Acetal (POM) Copolymer | Witcom POM-C |
| Axiall PVC 8895 | Axiall Corporation | PVC, Unspecified | Axiall PVC |
| LUVOCOM® 19-7278 | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |