Sup-tech CT703
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | W5N36D_Sup-tech-CT703.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech CT703 is a Polycarbonate + PBT (PC+PBT) product filled with 15% glass fiber. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 4.0E-3 to 0.10 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 0.10 | % | |
| Saturation, 23°C | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 85.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 3.0 | % | DIN 53452 |
| Flexural Modulus | 4800 | MPa | DIN 53457 |
| Flexural Stress | 125 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 11 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 155 | °C | |
| 1.8 MPa, Unannealed | 140 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Electric Strength | 16 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 7.0 to 18 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Tuff-X 200 HG | Primex Plastics Corporation | Unspecified | Prime Tuff-X |
| NEXT REPROCESSED POMC M270-300R | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REPROCESSED |
| INSTRUC PPAGF30 | Infinity LTL Engineered Compounds | PPA | INSTRUC |
| Innova N 2560 | Innova SA | PS (GPPS) | Innova |
| Sylvin 9077-70 Yellow 4113 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |